1. The tempered glass cannot be cut or processed again. It can only be processed to the desired shape before tempering, and then tempered.
Although tempered glass has stronger strength than ordinary glass, it has the possibility of self explosion (self rupture), while ordinary glass does not have the possibility of self explosion.
3. The surface of tempered glass may have unevenness (wind spots) and slight thinning of thickness. The reason for thinning is because after the glass is softened by hot melting, it is rapidly cooled by strong wind, causing the crystal gap inside the glass to decrease and the pressure to increase. Therefore, the glass is thinner after tempering than before. In general, 4-6mm glass thins by 0.2-0.8mm after tempering, while 8-20mm glass thins by 0.9-1.8mm after tempering. The specific degree depends on the equipment, which is also the reason why tempered glass cannot be used as a mirror.
4. Flat glass used in construction after physical tempering in a tempering furnace generally undergoes deformation, and the degree of deformation is determined by the equipment and technical personnel's process. To some extent, it affects the decorative effect (except for special needs).